The Influence of Friction Stir Welding and Process Parameters on the Static and Dynamic Mechanical Properties of 2024-T3 Aluminum Alloy Weldments | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 30, Issue 4, February 2012, Pages 556-567 PDF (264.09 K) | ||
| DOI: 10.30684/etj.30.4.3 | ||
| Authors | ||
| Nameer A.Hamoody; Moneer H.Tolephih; Shaker S. Hassan | ||
| Abstract | ||
| The present work is aimed to study the friction stir welding and process for the aluminum alloy 2024-T3, a threaded pin with a diameter of 6 mm and a concaved shoulder of 18 mm welding tool was used. The single pass friction stir welding (FSW) process was performed with clockwise tool rotation at different speeds and variable feeding speeds. The specimens were tested to determine the best ultimate tensile strength ( ult) and compared with the as received metal. In addition to friction stir welding (FSW), another phase of welding named friction stir process (FSP) was used. The best condition out of the FSW variables was selected in order to examine the double pass welding processes. It was found that the best result is in forward welding travel and counterclockwise tool rotation. The maximum tensile strength achieved at friction stir welding process was 72% of the base metal and didn’t improve in the FSP process. On the other hand, the fatigue endurance limit was improved for FS weld ment when followed by FSP, where the reduction in fatigue endurance limit for FSW specimen was 36% while for FSP specimen was 15% of the base metal. | ||
| Keywords | ||
| Friction stir welding; Double pass; Aluminum Alloy | ||
|