Studying the optical properties of tZnxCd1 – x S thin films prepared by chemical bath deposition (CBD) and the effect of annealing temperature. | ||
| Journal of University of Anbar for Pure Science | ||
| Article 42, Volume 7, Issue 2, August 2013, Pages 1-6 PDF (671.41 K) | ||
| Document Type: Research Paper | ||
| DOI: 10.37652/juaps.2013.84998 | ||
| Author | ||
| Ibrahim J.Abdulleh* | ||
| University Of Anbar - Education college for pure science | ||
| Abstract | ||
| The ZnxCd1 – x S (x=0.2,0.5,0.7) thin films have been deposited by chemical both deposition method on glass substrates from aqueous solution containing cadmium acetate , zincacetate and thiourea at 80±5 ℃and after annealed at 150-200 ℃. optical method was used to determine the band gap of films between 3.95 to 4.1 eV. The UV-VIS spectra of films have been studied and the result are discussed. | ||
| Keywords | ||
| studying; the optical properties; ZnxCd; Thin films; prepared by; deposition; Annealing Temperature | ||
| References | ||
|
1.T.Prem, S.Sarvanakumar, K.Sankarana rayanan, Applied surface science 257 (2011) 1923 – 1927 .
2.S.Stolyarova, M.Weinstein, Y.Nemirovsky, Journal of Crystal Growth 310 (2008) 1674 – 1678 .
3.T.Chandra, S.Bhushan, J.Mater . Sci.39(2004)6303 .
4.T.Carlsson, A.Brinkman, prog. Photovolt. 14(2006)213 .
5.Y.Raviprakash, Kasturi V.Bangera, G.K. Shivakumar, SolarEnergy 83 (2009)1645 – 1651 .
6.N.Karar,Mathuresh Jayaswal, .K.Halder ,HarishChander,Journal of Alloys and compounds 436(2007)61 – 64 7.R.Mariappan,M.Ragavendar,V.Ponnuswamy,Journal of Alloys
8.S.D.Chavhan,S.V.Bagul,R.R.Ahire,N.G.Deshparde,A,A,Sagat,Y.G.Guade,Rampral Sharma Journnal of Alloys and compounds 436(2007)400-406.
9.M.Bem Rabeh,M.Kanzarian and B.Rezig, J.Optoelectronic and Biomedical material; vol.1,no1(2009),pp70-78.
10.M.Celattin Baykul, Nigunorhan thin solid films 518(2010) 1925-1928.
11.Mahrov,B,G.Boschloo,A.Hgfeldt,L.Dloczuk,and Th.Dittrich Appl.phys. lett.84 (26)(2004)5455-5457.
12- G.B. Sakr, I.S. Yahiaa, M. Fadel, S.S. Fouad, N. Romˇcevi´c, J. of Alloys and Compounds, 507 (2010) 557–562.
| ||
|
Statistics Article View: 246 PDF Download: 196 |
||