Evaluation of the effect of intermediate agents on the shear bond strength of repaired aged silorane resin composite | ||
| Journal of baghdad college of dentistry | ||
| Article 1, Volume 24, Issue 4, December 2012, Pages 8-13 | ||
| Authors | ||
| Hanaa A. Saleh; Luma M. Baban | ||
| Abstract | ||
| Background: The aim of this study was to evaluate the bonding effect of different intermediate agents on the bond strength of silorane resin composite (Filtek™ P90,3M ESPE) that repaired by either silorane (Filtek™ P90) or methacrylate based resin composite (Filtek™ Z250,3M ESPE) Materials and Methods: Eighty specimens of resin composite prepared by filling silorane (Filtek™ P90) into a retentive cavity (6mm in diameter and 2mm in depth) of acrylic mold. The composite were polymerized, water stored at 37°C for one week. Their surface were finished with medium (violet) super-snap disks then rinsed in ultrasonic cleaner. Repair was performed with either silorane (Filtek™ P90) or methacrylate based composite (Filtek™ Z250) by using several intermediate agents which include (P90 System Adhesive, Adper Scotchbond Multipurpose and Clearfil repair kit).The shear bond strength (crosshead speed 0.5 mm/min) was measured after an additional water storage of 24 hour. Results: Statistical analysis of data revealed that intermediate agents enhanced the bond strength significantly (p<0.001).The highest shear bond strength were determined for Clearfil repair kit and P90 System Adhesive which were significantly higher than the control (p<0.001). Adper Scotchbond Multipurpose enhanced the bond strength significantly than the control but it was significantly lower than the other adhesive systems (p<0.001). Conclusions: The Clearfil™ Repair kit and P90 System Adhesive were the most effective intermediate agents for repair of silorane restoration with both silorane and methacrylate repair materials.Use of Adper Scotchbond Multipurpose resulted in bond strength which is considered clinically inadequate | ||
| Keywords | ||
| Intermediate agents; Repair; Bond strength; Silorane | ||
|
Statistics Article View: 36 PDF Download: 15 |
||