The effect of autoclave processing on some properties of heat cured denture base material | ||
| Journal of baghdad college of dentistry | ||
| Article 1, Volume 24, Issue 3, October 2012, Pages 13-17 | ||
| Authors | ||
| Salwan S. Abdulwahhab; Widad A.H. Alnakkash | ||
| Abstract | ||
| Background: Although most of the physical and mechanical properties of denture base resin polymerized by the conventional heat polymerization have been studied, the effect of autoclave processing in these properties has not been fully determined. The aim of the present study is to investigate the effect of two different cycles of autoclave processing on the transverse strength, impact strength, surface hardness and the porosity of acrylic denture base material. Materials and methods: Vertex was the heat- cured acrylic denture base material included in the study. A total of 120 specimens were prepared, the specimens were grouped into: Control groups (Group A) in which acrylic resins processed by conventional water- bath processing technique (74°C for 1.5 hours then boil for 30 minutes) and experimental groups in which acrylic resins processed by autoclave at 121°C,210KPa.The experimental groups were divided into Group B(Fast) for15min. , and Group C (Slow) for 30min... To study the effect of the autoclave processing (Tuttnauer 2540EA), four tests were conducted transverse strength (Instron universal testing machine), impact strength (charpy tester), surface hardness (shore D), and porosity test. The results were analyzed to ANOVA and LSD test. Results: There were no significant differences between the results of the processing techniques regarding transverse, impact, and hardness tests. While, there were a highly significant difference in porosity test results. Conclusions: The autoclave processing technique might also be a good alternative to the conventional water bath processing technique. Regarding to autoclave processing technique, the slow (long) curing cycle provide better denture bases material including the tested physical and mechanical properties as compared with the fast (short) curing cycle. | ||
| Keywords | ||
| Autoclave; Transverse; impact; Hardness; porosity | ||
|
Statistics Article View: 203 PDF Download: 169 |
||