Hubi Haleem, A., Zuheir, N., Muhammad Dawood, N. (2012). Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles. Alustath, 20(1), 30-38.
Ali Hubi Haleem; Newfal Zuheir; Newal Muhammad Dawood. "Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles". Alustath, 20, 1, 2012, 30-38.
Hubi Haleem, A., Zuheir, N., Muhammad Dawood, N. (2012). 'Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles', Alustath, 20(1), pp. 30-38.
Hubi Haleem, A., Zuheir, N., Muhammad Dawood, N. Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles. Alustath, 2012; 20(1): 30-38.

Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Journal of University of Babylon
Article 1, Volume 20, Issue 1, February 2012, Pages 30-38
Authors
Ali Hubi Haleem; Newfal Zuheir; Newal Muhammad Dawood
Abstract
The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditions
Results were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.
Keywords
MMCS; composite; powder metallurgy; aluminum; Mechanical properties