Evaluation of Corrosion Résistance for Austenitic Stainless Steel Weldment in Different Solution | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 30, Issue 17, October 2012, Pages 369-381 PDF (600.52 K) | ||
| DOI: 10.30684/etj.30.17.15 | ||
| Author | ||
| Entisar Mohson Hameed | ||
| Abstract | ||
| This paper is amid to study the effect of immersion solusion type on corrosion resistance of austenitic stainless steel AISI 304L . The process welding carried out on sheet metal by using four types of electrodes (E308L,E309L,E312,E347) to obtain butt joint welding under constant conditions polarity(DCSP) , voltage(30)v, current (120)A . Welding speed (100) mm/min and two weld passes by using electrode of diameter 3 mm. Many specimens for corrosion test were manufactured in (20*20*8) mm from welding joint stainless steel. Corrosion test was implemented by using weight loss, specimens were immersed in two solution (1% H2SO4) Sulphric Acid and (3.5%Nacl) sea water for (1-30 ) days and corrosion rate was measured. The results show that sulphric acid was more effected on stainless steel. | ||
|
Statistics Article View: 154 PDF Download: 47 |
||