Study of some Physical properties of basalt – clay mixes | ||
Journal of University of Anbar for Pure Science | ||
Article 23, Volume 3, Issue 1, April 2009, Pages 75-78 | ||
Document Type: Research Paper | ||
DOI: 10.37652/juaps.2009.37701 | ||
Author | ||
Adil N . Ayyash* | ||
University Of Anbar – collage of science | ||
Abstract | ||
Jordanian basalt was added to China clay on different mixes up to 60% by weight. Some of physical properties were studied. Mixes basalt showed a remarkable increase in density with increasing basalt addition. Porosity was the property greatly affected with increasing the firing temperature. Maximum reduction in porosity was observed at high firing temperature for all mixes and this will cause increase in hardness values. The different phases were determined by X–ray analysis. The expansion coefficient decreases with the increase of the basalt content. No significant differences of the heating rate are observed on the properties of the thermal expansion after firing at 1100°C for all mixes. | ||
Keywords | ||
Physical; basalt; mixes | ||
Supplementary Files
|
||
References | ||
1-W.A.Deer,R.A.Howie and J.Zussman, An Introduction to the Rock Forming Minerals, Longman Book Society, London (1990).
2-A.Wagdi and A-El-Shennawi, Monopyroxenic Basalt –Based Glass –Ceramics, J. Amer.Ceram.Soc, 82, (1999).
3-K.Horai, Thermal Conductivity of Rock Forming Minerals, J.Geophys. Res, 76,1278, (1971).
4-W.Botton,Engineering Materials Technology, 3th Ed, Butter Worth Heinman,(1998).
5-K.Gamlen and S.Lyng, the properties of the firing rate on basalt, J.Brit. Ceram.Soc, 73,139, (1974).
6-N.G.Holmstron, Ceram. Bull,60, 470, (1981).
7-C830, Annual Book of ASTM Standards, American Society for Testing and Materials, U.S.A., Vol. 15.01, (1988).
8-Basalt Product Information, Lbarrie Canada Limited, Internet Sit [http: // www. Brodeurmachina. Com / coating. html]. (2003). E-mail:albarrie@albarrie.com.
9-G.Piatti, Advance in Compositr Material, Applied Scince Publisher LTD, London (1999).
| ||
Statistics Article View: 258 PDF Download: 34 |