Studying the Efficiency of Lime-Soda Sinter Process to Extract Alumina from Colored Kaolinite Ores Using Factorial Technique of Design of Experiments | ||
Engineering and Technology Journal | ||
Article 4, Volume 36, 5A, May 2018, Pages 500-508 PDF (890.51 K) | ||
DOI: 10.30684/etj.36.5A.4 | ||
Authors | ||
Hijran Z. Toama* 1; Abdul-Wahab A. Al-Ajeel2; Ajheen H. Jumaah1 | ||
1Production Engineering & Metallurgy Dept., University of Technology, Baghdad, Iraq | ||
2Iraqi Geological Survey Baghdad, Iraq | ||
Abstract | ||
As the increasing demand for alumina in recent years with the result diminishing reserve of bauxite, the need to secure a domestic raw material base is driving research in new technologies to process low grade ores into alumina, with the intention that these technologies will lead to a significant reduction of bauxite and alumina transportation costs, allow the extraction of more valuable components from the ore and reduce environmental impact. Clays are types of the low-grade aluminum ores, they're also well abundant which make them a potential substitutes for Bauxite. In this work, lime soda sinter process was adopted for extracting alumina from kaolinitic claystone from Al-Ga'ara formation (Duekhla) quarry in western Iraq. The operation efficiency of sintering was studied in which the whole process has been done with three stages: the sintering process for the raw materials, leaching and carbonizing processes to precipitate and separate the alumina from the leach pregnant solution . Factorial technique of Design of Experiments (DOE) module in Minitab was used as a principal methodology to examine the sintering efficiency over alumina extraction. The results obtained showed that the optimum parameters for the sintering operation were CaO/SiO2 molar ratio of 2.2, Na2O/Al2O3 molar ratio of 1.2, sintering temperature at 1213 °C for 90 min. The sintered materials were leached with sodium carbonate solution, and sodium aluminate solution was obtained. By bubbling carbon dioxide gas into this extract solution aluminum hydroxide [Al(OH)3] has been precipitated and on calcination at 1200 °C for 2 hrs, alpha alumina (α-Al2O3) was obtained with purity of 98.5 %. | ||
Keywords | ||
Lime-soda; kaolin; Extract Alumina; DOE; Factorial Technique | ||