Mechanical Properties of Welded Martensitic Stainless Steel (AISI420) Subject to Different Heat Treatment | ||
| Anbar Journal of Engineering Sciences | ||
| Article 3, Volume 11, Issue 1, May 2020, Pages 12-18 PDF (1.74 M) | ||
| Document Type: Research Paper | ||
| DOI: 10.37649/aengs.2020.171279 | ||
| Authors | ||
| J. Jamal; H. Ali; S. Hareer | ||
| Materials Engineering Department, University of Technology, Iraq | ||
| Abstract | ||
| The aim of this article is to investigate the properties for joints of welded martensitic stainless steel (MSS) by ER 309 L filler wire, using tungsten arc welding (Tig). The regions of the base and welded materials were investigated by means of SEM, EDS, OP and HV were conducted to calculate the properties of the welded specimens. The influence of heat and cryogenic treatments also investigated, The best results from microstructure side occurrence epitaxial grains growth which was observed along the interface of weld-metal region, the maximum hardness was (414 HV) in conventional heat treated samples that tempered at 200°C, precipitation of small carbides were observed that this is responsible for the improvement in the mechanical properties of the material. Hardness at the HAZ region in state of DCT in all weldments was reduced as compared to hardness of HAZ region of CHT. The microhardness was at the highest value in the fusion zone | ||
| Keywords | ||
| Martensitic Stainless Steel; MSS; Cryogenic Treatment; Hardness; Post Weld Heat Treatment; PWHT | ||
|