The Influence of Ultrasonic Impact Peening on the Mechanical Properties of Similar Friction Stir Welded Joints of AA 7075-T73 | ||
| Engineering and Technology Journal | ||
| Article 2, Volume 39, Issue 9, September 2021, Pages 1345-1351 PDF (958 K) | ||
| Document Type: Research Paper | ||
| DOI: 10.30684/etj.v39i9.1725 | ||
| Authors | ||
| Abdul Ameer H. Jebur* 1; Samir A. Amin2; Ibtihal A. Mahmood | ||
| 1Institute of Tech. , Middle Technical University, Baghdad, Iraq. | ||
| 2Mech. Eng. Dept, University of Technology, Baghdad, Iraq. | ||
| Abstract | ||
| The purpose of this study is to study the ultrasonic peening influence upon the mechanical properties of the welded joints of 3 mm AA 7075-T73. Friction stir welding (FSW) was carried out by using milling machine and cylindrical tool with tapered pin. The used welding parameters were 710 rpm , 35 mm min for rotational and travel speed , respectively .Tensile tests results showed that the welding efficiency was about 60% for welded samples , and this value increased by using one and two lines ultrasonic peening treatment to 74% , and 71% , respectively , this improvement is due to generating compressive stresses along the surface of welded joints. The microhardness of the welded samples showed that there were fluctuations across the welded centerline and minimum hardness occur in the heat affected zone (HAZ). | ||
Highlights | ||
| ||
| Keywords | ||
| Aluminum Alloy; Friction stir welding; Ultrasonic Peening; Mechanical properties | ||
| References | ||
|
[1] I. Shigematsu, Y. J.Kwon, K Suzuki, T. Imai and N. Saito, “Joining of 5083 and 6061 aluminum alloys by friction stir welding,” Journal of Materials Science Letters 22, pp. 353-356, 2003. [2] M. Guerra, C. Schmidt, L.C. McClure, L.E. Murr and A. C Nunes, "Flow patterns during friction stir welding," Materials Characterization 49, pp. 95-101, 2003. [3] Alloy 7075 plate and sheet, 2007. [4] C. Blawert, N. Hort and K.U. Kainer, “Automotive Applications of Magnesium and its Alloys,” Trans. Indian Inst. Met. Vol. 57, No. 4, pp. 397–408, August 2004. [5] R. Roth, J. Clark and A. Kelkar, “Automobile bodies: Can aluminum be an economical alternative to steel?” JOM, 53, pp. 28–32, 2001 [6] R.S. Mishra and Z.Y. Ma, “Friction stir welding and processing,” Materials Science and Engineering: R. Vol.50, No. 1-2 pp. 1–78, August 2005. [7] J. G. Perrett, J. Martin, P. L. Threadgill and M.M.Z. Ahmed, “Recent Developments in Friction Stir Welding of Thick Section Aluminum Alloys,” The 6th World Congress, Aluminum Two Thousand, Florence, Italy, 13-17 March 2007. [8] P.L.Threadgill, “Friction stir welds in aluminum alloys–preliminary microstructural assessment,” TWI Bull., 28, pp. 30–33, 1997. [9] M. Kadlec, R. Růžek and L. Nováková., “Mechanical behavior of AA 7475 friction stir welds with the kissing bond defect,” Int. J. Fatigue, Vol. 74, pp. 7–19, 2015. [10] T. Le Jolu, T. F. Morgeneyer, A Denquin, M. Sennour, A Laurent, J. Besson and A. F. Gourgues-Lorenzon, “Microstructural characterization of internal welding Defects and their effect on the tensile behavior of FSW joints of AA2198 Al–Cu–Li alloy,” Metal & Mater. Trans. A., 45, 12, pp. 5531–44, 2014. [11] R. Mishra, M.W. Mahoney, Y. Sato, Y. Hovanski and R.Verma,“Friction Stir Welding and Processing VII,” John Wiley and Sons, 29 January 2013. [12] R. S. Mishra, Z.Y. Ma and I. Charit., “Friction stir processing: a novel technique for fabrication of surface composite,” Materials Science and Engineering A, Vol. 341, No.1-2, 20 January 2010. [13] M. Massoud and H. Ding, “A review of ultrasonic peening treatment,” Materials & Design, Vol. 87, pp.1072–1086, December 2015. [14] R. Zhang, X. Li, Y. Liu, C. He and Q. Wang, “Effect of Ultrasonic Peening Treatment on VHCF Behavior of Friction Stir Welded Joints in Aluminum Alloys,” IOP Conf. Series: Materials Science and Engineering 611,012011, Wuhan, china, 19-21 July 2019. [15] L. Chuan, C. Dongjun, R. Michael, N. Minh and Z. Jiasheng, “Effects of ultrasonic impact treatment on weld microstructure, hardness, and residual stress,” Materials Science and Technology, Vol. 33, No. 14, pp. 1601–1609, 2017. . [16] Hangzhou Create Ultrasonic Technology Co. Ltd, “Ultrasonic Generator, Ultrasonic pre stressing force impact treatment system,” Operation instruction.WW. hzcreate. eng. Alibaba.Com, 2013. [17] ASM Handbook, “Metallography and Microstructures,” American Society for Metals, Vol. 9, 2004. [18] Standard Test Methods for Tension Testing of Metallic Materials, E8M-09, ASTM, 2010. [19] Standard Test Method for Vickers Hardness of Metallic Materials, E92–82, ASTM, 2003. [20] Standard Reference Radiographs for Inspection of Aluminum and Magnesium Castings, E155, ASTM, 2014. [21] R.K.R. Singh, C. Sharma, D.K. Dwivedi , N.K. Mehta, and P. Kumar , “The microstructure and mechanical properties of friction stir welded Al–Zn–Mg alloy in as welded and heat treated conditions,” Journal Materials and Design, Vol. 32, No.2, pp. 682-687, 2011. [22] A. Barcellona, G. Buffa., L. Fratini, and D. Palmeri, “Microstructural phenomena occurring in friction | ||
|
Statistics Article View: 365 PDF Download: 404 |
||