Studying the Erosion Corrosion Behavior of NiCrAlY Coating Layer Applied on AISI 446 Stainless Steel Using Thermal Spray Technique | ||
| Engineering and Technology Journal | ||
| Article 10, Volume 38, 11A, November 2020, Pages 1676-1683 PDF (1.11 M) | ||
| Document Type: Research Paper | ||
| DOI: 10.30684/etj.v38i11A.1691 | ||
| Authors | ||
| Ghufran J. Matrood1; Ahmed M. Al-Gaban1; Hussain M. Yousif2 | ||
| 1Materials Engineering Department, University of Technology, Baghdad, Iraq, | ||
| 2Ministry of Industry and Minerals, State Company for Steel Industries, Baghdad, Iraq. | ||
| Abstract | ||
| Erosion-Corrosion behavior of NiCrAlY coatings deposited on 446 stainless steel samples by flame thermal spraying was performed in this research. The hardness of uncoated and coated sample is measured, using HVS-1000 Digital Micro hardness Tester. The results of hardness show that the coated samples have higher hardness than uncoated samples. Microstructure and phase analysis of the coating layer was observed by using optical microscope, X-ray diffraction (XRD), and SEM respectively. Erosion –Corrosion test was performed in different period of time (6, 12, and 18 hr.) using the erosion-corrosion system. The result shows that because of uniform distribution and homogeneous of coating layer, weight loss was very low and approximately equal in all period of testing time. | ||
| Keywords | ||
| NiCrAlY coating; Molybdenum; erosion corrosion resistance; flame thermal spray | ||
| References | ||
|
[1] S. Rajahram, T. Harvey, and R. Wood, "Erosion–corrosion resistance of engineering materials in various test conditions," Wear, Vol. 267, No. 1-4, pp. 244-254, 2009. [2] R. Wood, “Erosion–corrosion interactions and their effect on marine and offshore materials,” Wear, Vol. 261, No. 9, pp. 1012-1023, 2006. [3] G. Burstein, and K. Sasaki, “Detecting electrochemical transients generated by erosion–corrosion,” Electrochemical Acta, Vol. 46, No. 24-25, pp. 3675-3683, 2001. [4] S. Rajahram, T. Harvey, and RWood, “Evaluation of a semi-empirical model in predicting erosion–corrosion,” Wear, Vol. 267, No. 11, pp. 1883-1893, 2009. [5] K. Sasaki, and G. Burstein, “Erosion–corrosion of stainless steel under impingement by a fluid jet,” Corrosion Science,Vol. 49, No. 1, pp. 92-102, 2007. [6] S. B. Mishra, K. Chandra, and S. Prakash, “Erosion–corrosion performance of NiCrAlY coating produced by plasma spray process in a coal-fired thermal power plant,” Surface and Coatings Technology, Vol. 216, pp. 23-34, 2013. [7] Takeda, M. KoichiIto, S. Takeuchi, K. Sudo, M. Koga, and K. Kazama, “Erosion resistant coating by low pressure plasma spraying,” ISIJ international, Vol. 33, No. 9, pp. 976-981, 1993. [8] M. Rosso, A. Scrivani, D. Ugues, S. Bertini, and H. Materials, “Corrosion resistance and properties of pump pistons coated with hard materials,” International Journal of Refractory Metals and Hard Materials,Vol. 19, No. 1, pp. 45-52, 2001. [9] A. Schnell, C. Bezencon, M. Hoebel, A. S. Khan, M. Konter, and W. Kurz, "Method of growing a MCrAlY-coating and an article coated with the MCrAlY-coating," US Patents 7014923, March 21, 2006. [10] K. Yuan, "Oxidation and corrosion of new MCrAlX coatings: modelling and experiments,” Ph.D. thesis, Linköping University, Sweden, 2014. [11] G. Antipas, “Spray forming of al alloys: Experiment and theory,” Materials Research, Vol.15, No.1, pp. 131-135, 2012 [12] L. Pawlowski,"The science and engineering of thermal spray coatings", John Wiley & Sons, 2nd edition, England, 2008. [13] A. S. Fakhri, A. M. Al-Gaban, and H. M. Yousif, "Oxidation behavior of NiAl coatings stainless steel by flame thermal spray", 1st conference on modern electrical, mechanical engineering systems and applications, Baghdad-Iraq 2019. [14] E.Sadeghimeresht, L. Reddy, T. Hussain, M. Huhtakangas, N. Markocsan, & S. Joshi, "Influence of KCl and HCl on high temperature corrosion of HVAF-sprayed NiCrAlY and NiCrMo coatings," Materials & Design, Vol. 148, pp. 17-29, 2018. | ||
|