Effect of Staining and Bleaching on Surface Roughness of Different Nano Hybrid Resin Composite Materials | ||
| Al-Rafidain Dental Journal | ||
| Article 5, Volume 21, Issue 1, March 2021, Pages 42-50 PDF (538.51 K) | ||
| Document Type: Research Paper | ||
| DOI: 10.33899/rden.2020.127506.1042 | ||
| Authors | ||
| Zahraa S Abdulwahhab* ; Emad Farhan Alkhalidi | ||
| Conservative Dentistry /Mosul University /Mosul /Iraq | ||
| Abstract | ||
| Aims: The purpose of this study was to evaluate the effects of staining by coffee and In-office bleaching by 30% hydrogen peroxide on surface roughness of two different Nano-Hybrid resin composite materials. Materials and Methods: In this in vitro experimental study, 32disc samples were fabricated from each type of the Nano-Hybrid resin composite materials, each sample measured 5 mm in diameter and 2 mm in height. The samples for each composite group were then sub-divided randomly into four sub-groups (n=8). In control sub-groups, samples were stored in artificial saliva at 37°C for 1 week. Samples of Staining sub-groups were stored in a coffee solution for 48h at 37°C. Samples of Staining Bleaching sub-groups were stained in a coffee solution for 48 h at 37°C then bleached with 30% H2O2. Samples of Bleaching sub-groups were bleached with 30% H2O2. The surface roughness measurements were taken for all samples of each sub-group; the measurements for control sub-groups considered as baseline data. Results: The surface roughness measurements of all sub-groups for both tested materials didn’t exceed the critical value (Ra< 0.2 μm) with no significant difference among all sub-groups (P >0.05). Conclusion: Surface roughness of the two tested Nano-Hybrid resin composite materials were neither influenced by coffee staining nor by in-office bleaching with 30% H2O2. | ||
| Keywords | ||
| Resin composite,,; ,،,؛staining,,; ,،,؛bleaching,,; ,،,؛hydrogen peroxide,,; ,،,؛Surface Roughness | ||
|