IMPROVEMENT OF MECHANICAL PROPERTIES OF ALUMINUM ALLOY 6061 –T6 WELD JOINT USING DC PULSED GAS TUNGSTEN ARC WELDING (PGTAW) | ||
| Iraqi journal of mechanical and material engineering | ||
| Article 1, Volume 18, Issue 2, December 2018, Pages 331-338 | ||
| Authors | ||
| Jenan Mohammed Naje; Hamdiyah Majeed Mohammed; Nidaa Hameed Dawood | ||
| Abstract | ||
| The effect of DC pulsed GTAW method factors on mechanical properties of Aluminum alloys 6061–T6 is proves. Throbbed GTAW on the sheet having dimension of (200* 100* 5mm) is implemented at variable pulse current (150, 160, 170, 190) and constant frequency to get numerous connected joints by electrode type" ER4043 (Al Si5) as a padding metallic and argon as protective gas and compared with base current GTAW welding at D C current at 90 amps. The welded pieces are examined by X-ray radiography. The welded joints were treated by heat, the joints heated for half an hour in the furnace to 150 C° then cooled in the air to release the residual stresses. Mechanical quality of the weld joints. Microstructural categorizations, Micro hardness, enduring stress are examined. Consequences exposed that a common decline of mechanical properties of TIG welded joints conveyed 34% analogies with parent metal while the PGTAW joined offers better mechanical qualities analogy with of TIG joined in reductions conveyed 8.4% analogies with original metal this is because of the microstructure variations through the joining method and compressive residual stress generation in the weld zones. It has been found that by PGTAW improved the mechanical properties of welded joints which rely on current parameters | ||
| Keywords | ||
| GMAW; Pulsed current; Aluminum Alloy; Microstructure; Mechanical properties | ||
|
Statistics Article View: 44 PDF Download: 1 |
||