Some Mechanical Properties of Reactive PowderLight Weight Concrete | ||
| Anbar Journal of Engineering Sciences | ||
| Article 4, Volume 4, Issue 1, May 2011, Pages 47-61 PDF (236.14 K) | ||
| DOI: 10.37649/aengs.2011.14248 | ||
| Author | ||
| Ibrahim A. S. Al-Jumaily | ||
| Abstract | ||
| In General, original reactive powder concrete (RPC) consists of a superplasticized cement mixture with silica fumes, steel fiber and ground fine sand (150-600 ىm). The main purpose of the present work is to produce and study some mechanical properties of lightweight reactive powder concrete using a superplasticized cement mixture with high reactivity metakaolin (HRM) instead of silica fume, steel fiber (with different ratios ) with ground fine sand (150-600 ىm) and light weight material called (Perlite ) also with different ratios .This investigation was carried out using several tests, these tests were compressive strength, modulus of rupture, modulus of elasticity, density and absorption, and performed for specimens at ages of 3, 7, 28 days, respectively. The tests results were compared with a reference mix. The experimental results shows that , with different ages, (for constant Perlit ratio for 0% to 10% as additional cementtitious materials) addition of 1% steel fiber will improve about (8.3%-10% , 3.2%-11%and 0.25%- 8%) for compressive strength , modulus of rupture, and modulus of elasticity respectively, and increase density, absorption about (0.8%-1.8%,4.5%-8.2%) respectively. Also an increase of steel fiber ratio to 2% will improve about (16.5%-20.3%, 9.0%-17%, and 1.7%-11.5%) for compressive strength , modulus of rupture and modulus of elasticity respectively, and increase density, absorption about (1.7%-2.3% , 7.3%-8.3%) respectively. For same steel fiber ratio about 0% to 2%, increasing Perlite ratio to 2.5% will decrease about (17.3%-18.8%, 9.5%-15.5%, 4.4%-16.6%, and 4.98% - 6.9%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption to about (55.5% - 66.5%). Increasing the ratio to 5% will also make a decrease of about (36%-36.77%, 33.7%-37%, 16.5%- 21.88%and 15.91%-19.74%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption for about (106%- 110.5%) . Increasing the ratio to 10% will also decrease about (45.98%-47.2%, 46.5-54.2%, 30.6%- 35.57%and 19.4%-23.36%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption about(183%- 192.6%). To produce structural lightweight concrete, the tests results show that the optimum steel fiber is 1% by volume and optimum Perlite ratio is 2.5% by weight of cement as additional materials. | ||
| Keywords | ||
| Reactive powder; Light weight concrete; Steel Fiber; Mechanical properties | ||
|
Statistics Article View: 282 PDF Download: 111 |
||