A Study the Effect of Addition of Silanized Zirconium Oxide Nanoparticles on Some Properties of High-Impact Heat-Cured Acrylic Resin | ||
| Journal of baghdad college of dentistry | ||
| Article 1, Volume 28, Issue 2, June 2016, Pages 19-25 | ||
| Authors | ||
| Soodad A. Al-Hiloh; Intisar J. Ismail | ||
| Abstract | ||
| Background: The incorporation of rubber has not been entirely successful because it can have detrimental effects on the transverse Strength and hence the rigidity of the denture base. Materials and methods: Zirconium oxide nanoparticales were coated with a layer of trimethoxysilylpropylmethacrylate (TMSPM) before sonication in monomer (MMA) with the percentages 3% by weight then mixed with powder using conventional procedure.(100) samples were prepared and divided into five groups according to the test performed ,Each group consisted of 20 specimens and these were subdivided into 2 groupsGroup (A): control group (10 specimens of high impact acrylic resin without zirconium oxide) and Group (B):zirconium oxide group(10 specimens of high impact acrylic resin with 3% wt zirconium oxide).The tests conducted were impact strength, transverse strength, indentation hardness(shore D), surface roughness, water sorption and solubility. The results were statistically analyzed using Dunntt t-test. Results: Highly significant increase in impact strength and transverse strength occurred with the incorporation of 3% wt Zirconium oxide nanofiller. A highly significant increase in surface hardness, but the water sorption and solubility were significantly decreased with the addition of silanized (ZrO2) Nano particles compared with the control group.no significant statistical difference in surface roughness. Conclusions: The addition of silanized ZrO2 Nano particles to high impact heat cure acrylic resin material improves the impact strength, transverse strength and surface hardness of high-impact heat-cure acrylic resin at the same time this addition decreases water sorption and solubility. On the other hand there was no change in surface roughness with the addition of 3% wt of silanized ZrO2Nano particles | ||
| Keywords | ||
| High impact heat cured acrylic resin; Zirconium oxide nanoparticales; nano composite | ||
|
Statistics Article View: 126 PDF Download: 72 |
||