Study the Mechanical and Physical Properties of Polyester Composite Reinforced by Multi Layers | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 34, 9A, September 2016, Pages 1834-1843 PDF (464.74 K) | ||
| DOI: 10.30684/etj.34.9A.10 | ||
| Authors | ||
| Fadhil Abbas Hashim; Mohammed Sellab Hamza; Reham Raad Abdulla | ||
| Abstract | ||
| In this research, a laminate composite has been prepared, using unsaturated polyester resin (UP) as a matrix reinforced with Kevlar fibers in different number of layers, glass fibers were added to the optimum product, by replacing one of the layers of Kevlar Fibers with a layer of Glass Fibers. Hand Lay-up method was used to prepare the test samples. To evaluate the composite material properties, tensile, hardness, impact, optical microscope tests were done. The results of composite made of polyester reinforced with Kevlar Fibers show that the mechanical properties (Tensile strength, Modulus of elasticity, Hardness, Impact strength) increase with increasing the number of reinforced layers. The best experimental values ofthe mechanical properties (Tensile strength, Modulus of elasticity, Hardness, Impact strength) were (190 MPa, 1.72 GPa, 79.25, and 68.75KJ/m2) respectively, for composite with three layers of Kevlar Fibers and then followed by composite with the sequence of layers (kevlar-glass-kevlar) and its mechanical properties (Tensile strength, Modulus of elasticity, Hardness, Impact strength) were (175.5 MPa, 1.69 GPa, 80, and 59.1 KJ/m2) respectively, Optical microscope shows welldistribution ofreinforcedlayers in composite. | ||
| Keywords | ||
| Laminate composite; Hybrid composite; Unsaturated polyester; Kevlar fiber; Glass Fibers; Tensile Strength; Modulus of elasticity; Hardness; Impact strength; and optical microscope | ||
|
Statistics Article View: 367 PDF Download: 79 |
||