Enhancement of DSSC by Using Gold Nanoparticles | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 34, 1B, January 2016, Pages 73-79 PDF (796.9 K) | ||
| DOI: 10.30684/etj.34.1B.8 | ||
| Authors | ||
| Ghufran S. Jaber; Abdulrahman K. Ali; Mukhlis M. Ismail | ||
| Abstract | ||
| In this research, AuNPs prepared by laser ablation in liquid (PLAL) at 750 mJ energy and 90 pulses. They have been added to N719-dye to form (Au-N719) mixture. TiO2 paste was deposited on FTO substrates and immersion in a mixture dye and AuNPs. DSSC was fabricated and enhancement of the DSSC conversion efficiency was achieved. Scanning electron microscope, X-ray diffraction and UV-Visible spectrophotometer were used to characterize and study the DSSC components. The UV-Vis data show high absorbance of AuNPs+N719 dye compared to N719 dye only; that means the immersion of AuNPs in the N719-dye solution tend to increase the total absorbance of the dye. The XRD pattern of AuNPs has diffraction peaks at 38.2° and 44.4° which can be indexed by (111), (200) plane of Au in the cubic phase. The shape and size distribution shows spherical AuNPs with particle size about (50-60) nm. The relative increase of short circuit current density after the adding gold nanoparticles was about 76%. In the same way the relative increase of open circuit voltage after adding gold nanoparticles was about 6.7%. The total photon-to-current energy conversion efficiency for the standard DSSC is 1.75 while its 2.8 of the enhanced DSSC with gold NPs.The maximum enhancement is about 60 % under illumination (105 mW/cm2, (AM1.5). | ||
| Keywords | ||
| PLAL; DSSC; AuNPs; Dye | ||
|
Statistics Article View: 216 PDF Download: 112 |
||