Aging effect of different types of composite resin restoration on shear bond strength to different orthodontic adhesives with sapphire bracket (In vitro comparative study) | ||
| Journal of baghdad college of dentistry | ||
| Article 1, Volume 26, Issue 2, June 2014, Pages 144-149 | ||
| Authors | ||
| Linda B. Jabbar; Fakhri A. Ali | ||
| Abstract | ||
| Background: This study was performed to determine the effect of aging of different types of composite material restorations on: Shear bond strength (SBS) to light cure and no mix chemical cure orthodontic adhesives with sapphire bracket and the debonding failure sites. Materials and methods: One hundred forty four composite disks were made from three different composite resin materials which are: 3M Filtek Z250, 3M filtek Z350 and 3M Valux plus, each group with (48) disks each, then according to the duration of storage each group was subdivided into two equal groups one of them stored for one day and the other was stored for one month, then each group was further subdivided into two equal subgroups with (12) disks each one bonded with light cure orthodontic adhesive and the other with no mix chemical cure adhesive. The sample was tested for bond strength using the universal testing machine and the Adhesive Remnant Index (ARI) was inspected under the stereomicroscope. Results: The results revealed that there was a highly significant difference among the three types of composite materials bonded with light cure orthodontic adhesive as showed by ANOVA test, while the T test showed that there was no significant difference between the two storage durations and also between the two orthodontic adhesives for both Filtek Z250 and Valux plus. Conclusions: The highest (SBS) values were obtained from Filtek Z350 samples than other two types of composite. All the samples stored for one day showed higher values of (SBS) than those stored for one month | ||
| Keywords | ||
| Shear bond strength; sapphire bracket; orthodontic adhesive | ||
|
Statistics Article View: 198 PDF Download: 32 |
||